Як визначити, чи перевищує концентрацію кислоти в резервуарі для занурення за допомогою стандарту?

To determine whether the acid concentration of the immersion pickling tank exceeds the standard, a comprehensive analysis needs to be conducted in combination with the process standards, detection methods and actual reaction phenomena. The following are specific methods: 1. Concentration threshold based on process standards Each pickling process (such as steel rust removal, metal surface activation, etc.) has a clear acid concentration range, and the process documents or formula requirements need to be confirmed in advance. For example: Hydrochloric acid pickling: The commonly used concentration in the steel industry is 10%~20% (mass fraction). If the measured concentration is greater than 25% or less than 8%, it is considered to exceed the standard. Sulfuric acid pickling: The concentration is usually controlled at 15%~25%. Exceeding 30% may accelerate metal corrosion and produce a large amount of hydrogen. If it is less than 10%, the rust removal efficiency will be significantly reduced. Mixed acid (such as hydrochloric acid + hydrofluoric acid): It needs to be controlled according to a specific ratio (such as HCl:HNO₃=3:1). If the concentration of a single acid deviates from the formula by ±10%, it will be judged as abnormal. 2. Laboratory test method (precise quantification) The most reliable way to judge is to analyze the concentration of acid by sampling: Titration method (chemical analysis) Principle: Titrate the acid with a standard alkali solution (such as NaOH) and calculate the acid concentration by the amount of alkali consumed. Operation steps: Accurately draw 10mL of acid with a pipette, inject it into a conical flask, and add 2~3 drops of phenolphthalein indicator. Titrate with a known concentration of NaOH standard solution (such as 0.1mol/L) until the solution is slightly red and does not fade for 30 seconds, and record the consumed volume V (mL). Judgment standard: If the calculated result exceeds the process allowable range (such as ±5% fluctuation), it is considered that the concentration exceeds the standard. Density method (applicable to strong acid) Principle: The concentration of acid is linearly related to density (such as the higher the concentration of concentrated sulfuric acid, the greater the density), and the density is measured by looking up the table for comparison. Operation steps: Use a densitometer (or hydrometer) to directly immerse in the acid, read the scale value, and measure the temperature at the same time (need to be calibrated to the standard temperature of 20℃). Refer to the "Acid Concentration - Density Comparison Table" (e.g., hydrochloric acid at 20°C, 20% concentration corresponds to a density of about 1.09g/mL). If the measured value deviates from ±0.02g/mL, the concentration may be abnormal. pH detection method (applicable to dilute acid or mixed acid) principle: acid concentration is negatively correlated with pH value (the higher the concentration, the lower the pH), but it should be noted that strong acids (such as hydrochloric acid and sulfuric acid) have a dissociation℃close to 100% at high concentrations, and may not be sensitive to pH changes (e.g., 20% hydrochloric acid pH≈-0.3, 15% hydrochloric acid pH≈-0.1), and need to be used in combination with titration. The pH of weak acids (such as hydrofluoric acid) is nonlinearly related to concentration and needs to be converted through a standard curve. 3. On-site rapid detection method (convenient qualitative) is suitable for real-time monitoring or scenarios without laboratory conditions: pH test paper/test strips Use a glass rod to dip acid and drop it on the test paper, compare the pH value with the standard color card, and combine process experience to determine whether the concentration is abnormal (for example, in steel pickling, hydrochloric acid pH>1 може бути недостатньою) . Тестовий документ про концентрацію кислоти (спеціальний тестовий папір) Деякі виробники надають тестовий папір для специфічних кислот (наприклад, тестового документа про концентрацію соляної кислоти), який розвиватиме колір після занурення в кислоту, безпосередньо відповідає діапазону концентрації (наприклад, 10%~ 15%, 15%~ 20%, тощо. The higher the acid concentration, the greater the ion concentration and the higher the conductivity. The "concentration-conductivity" curve is pre-calibrated, and when the measured value deviates from the curve by ±10%, it indicates that the concentration is abnormal. 4. Observe the reaction phenomenon to assist in judgment When the acid concentration is abnormal, the reaction between the workpiece and Кислота значно змінюється, яка може бути використана як попередня основа для судження: недостатня концентрація (низька) явище: швидкість генерації міхурів на поверхні заготовки сповільнюється (метал реагує з кислотою для генерування менше водню) . час для видалення іржі або дескалії ( Це спочатку було завершено за 30 хвилин, як і раніше не відповідає стандарту через більш ніж 1 годину) . зміна кольору кислотного розчину не очевидна (e . g .}, у забитті сталі, концентрація Fe²+ збільшується, а кислотний розчин не стає зеленим, як очікувалося) .}} фен -фенуна (epentment thinementor eprengentration thinemenon eprengentration thinemenon eprengentration thinemenon eprentmancen eprentmancen standard): the reaction is violent, a large number of bubbles are generated, and acid mist is volatilized (e.g., when the hydrochloric acid concentration is too high, obvious white mist appears above the tank). The surface of the workpiece is excessively corroded, and "blackening" and "holes" or abnormal weight loss appear (increased risk of hydrogen Embrittlement) {. Температура кислотного розчину піднімається аномально (якщо операція є неправильною при розведенні концентрованої сірчаної кислоти, вона може кип’яти через інтенсивне вивільнення тепла) . v . частоти частоти інспекції: у регулярному виробництві, або 2 рази за зміну (8 годин) {{32 Операція, необхідно перевіряти один раз кожні 2 ~ 4 години . Після підготовки нового кислотного розчину, додавання кислотного розчину або зміну матеріалу заготовки, концентрація повинна бути негайно перевірена .} Аномальність, заходи лікування (наприклад, додавання кислоти, розбавлення або заміну) повинні бути позначені . 6. Заходи безпеки Безпечна робота: носити кислотні рукавички та окуляри під час тестування, щоб уникнути бризки кислоти; Вилийте зразок кислоти повільно, щоб запобігти бризку . Температурний вплив: при тестуванні щільності або провідності температура кислоти повинна бути виправлена ​​до стандартної температури (наприклад, 20 градусів), інакше вона спричинить помилки (підвищення температури та щільність рідини зменшується) . складних факторів: якщо кислота містить велику кількість металів (наприклад, fe²+, fe³+). Метод повинен бути об'єднаний, щоб виправити результати . за допомогою всебічного судження вищезазначених методів, аномальна кислота може бути виявлена ​​в часі, щоб уникнути некваліфікованих кидків через недостатню концентрацію, або аварії безпеки, спричинених надмірною концентрацією (наприклад, надмірна корозія, оформлення водню) .}}